Abstract: Aureobasidium is omnipresent and can be isolated from air, water bodies, soil, wood, and other plant materials, as well as inorganic materials such as rocks and marble. A total of 32 species of this fungal genus have been identified at the level of DNA, of which Aureobasidium pullulans is best known. Aureobasidium is of interest for a sustainable economy because it can be used to produce a wide variety of compounds, including enzymes, polysaccharides, and biosurfactants. Moreover, it can be used to promote plant growth and protect wood and crops. To this end, Aureobasidium cells adhere to wood or plants by producing extracellular polysaccharides, thereby forming a biofilm. This biofilm provides a sustainable alternative to petrol-based coatings and toxic chemicals. This and the fact that Aureobasidium biofilms have the potential of self-repair make them a potential engineered living material avant la lettre. Key points: •Aureobasidium produces products of interest to the industry •Aureobasidium can stimulate plant growth and protect crops •Biofinish of A. pullulans is a sustainable alternative to petrol-based coatings •Aureobasidium biofilms have the potential to function as engineered living materials.
DOCUMENT
Vibrational and structural properties of lead-free piezoelectric (1-x)Na0.5Bi0.5TiO3–xCaTiO3 (0 < x < 1.00) solid solutions have been investigated using Raman spectroscopy and X-ray diffraction. Different anomalies were detected and analyzed taking into consideration the phase transition from rhombohedral to orthorhombic phase at room temperature. All Raman bands were interpreted through the variation in the peak positions (frequency) and the corresponding half-widths at half maximum (HWHM) as a function of x. XRD used as a complementary technique to Raman spectroscopy, showed that the rhombohedral – orthorhombic phase transition went gradually through an intermediate phase consisting of a mixture of rhombohedral (R3c) and orthorhombic (Pnma) structures and that the fraction of orthorhombic phase increased with CT composition. The results show that the morphotropic phase boundary (MPB) is located between 0.09 and 0.15.
DOCUMENT